Abrasion And Wear Resistant Steel Plates

Wear resistant steel is used in areas where there is likely to be a high degree of abrasion or wear of thesteelplate. Typical applications are in truck beds, attachments to diggers and earth movers and in processing applications in the mining industry. 

The key quality for wear resistant steels is their hardness. We sell wear plate according to its hardness measured on the Brinnell Hardness Test – usually in 400HB and 500HB grades. If your specification is to the Rockwell Test we can also advise. 

Steels with a high HB rating (Brinell hardness) are intended for applications where wear or abrasion resistance is important. The benefit of using an abrasion resistant steel is that that the plant, machinery or constructions working life can be extended considerably. This can significantly improve the reliability, durability and safety of structures and equipment. It also helps to reduce the maintenance costs associated with wear and breakdown of plant. 

400 HB steel is over 3 times harder than mild steel (120HB), but only a third as hard as stainless steel (1250HB). Example uses are for construction machinery, skips, bulldozers and excavators, buckets and conveyors. 

The steel is quenched which provides wear resistance; in order to improve hardness it may also be tempered. Lower HB’s generally provide good cold bending properties and good weld ability. Weld ability is not generally reduced as the hardness increases. 

Wear resistant steels are not appropriate for use at temperatures over 250°C as the heat can cause changes to the material properties. 

Testing is undertaken by firing 10mm steel or tungsten carbide ball at 29kN and the size of the resulting indentation is measured. Tests are carried out according to EN ISO 6506 or ASTM E10. The figures below are representative of 15mm thick 400HB and 500HB plates. 

C Max

Si Max

Mn Max

P Max

S Max

Cr Max

400 HB

0.15%

0.70%

1.60%

0.225%

0.01%

0.50%

500 HB

0.29%

0.70%

1.60%

0.025%

0.01%

1.00%

 

Ni Max

Mo Max

B Max

CEV

CET

400 HB

0.25%

0.25%

0.004%

0.37%

0.27%

500 HB

0.50%

0.30%

0.004%

0.62%

0.41%

Values are typical and for general information purposes only. 

Yields for 400HB steel are in the region of 1100 MPa with tensile strengths of about 1250 MPa. 

Wear resistant plates from Riddhi Impex  are available in the following dimensions and certificated to EN 10204 3.1 B, dependent on the product required. 
Brand name supplied by us is of TISCRAL / SAILHARD/ JISCRAL/ LAS07 / HARDOX / DILLIDUR / DUROSTAT / ABRASO / XAR AND Other well known brands.

 





copper
Sheets & Plates  |  Pipes  |  Bar & Wire  | Flanges  |  Pipe Fittings

» Stainless Steel Pipes & Tubes » Steel Coils and Sheet » Butt Weld Elbow » Forged Elbow » Lap Joint Flanges
» 304 Stainless Steel Pipes and Tube » Stainless Steel Plates » Butt weld Reducers » Forged Reducers » Long Weld Neck Flanges
» 304L Stainless Steel Pipes and Tubes » Alloy Steel Plates SA 387 » Butt weld Tee » Forged Tee » Orifice Flanges
» 304H Stainless Steel Pipes and Tubes » Mild Steel Plates and Carbon Steel Plates » Butt weld Stub Ends » Forged End Caps » Plate Flanges
» 310 Stainless Steel Pipes and Tubes » Abrasion and Wear Resistant Steel Plates » Butt weld Adapters » Forged Stub Ends » Slip on Flanges
» 316 Stainless Steel Pipes and Tubes » Boiler Quality Steel Plates » Butt weld Pipe Nipples » Forged Couplings » Socket Weld Flanges
» 316L Stainless Steel Pipes and Tubes   » Butt weld End Caps » Forged Plug and Bushing » Spectacle Flanges
» 316H Stainless Steel Pipes and Tubes     » Forged Boss » Threaded Flanges
» 321 Stainless Steel Pipes and Tubes     » Forged Union » Weld Neck Flanges
» 347Stainless Steel Pipes and Tubes     » Forged Steel Adapters  
» 410 Stainless Steel Pipes and Tubes     » Forged Pipe Nipples  
» Alloy Steel Pipes & Tubes        
» Mild Steel Pipes & Tubes        
» ERW Pipes & Tubes